Influence of mineral aggregate concentration on the technological properties of fresh concrete mixture

Abstract

The main aim of this research was to investigate how the concentration of mineral aggregate influences the technological properties of concrete mixture such as: slump, flow characteristics and air content, as well as the density of concrete mixture. To sum up, 18 concrete mixture compositions were casted. First six compositions were casted in order to establish the dependence between the ratio of fine aggregate (sand fraction: 0/1 and 0/4) and the technological properties of fresh concrete mixture. Another six compositions were casted in order to investigate the link between course aggregate (gravel, fraction 4/16) concentration and the concrete mixture's technological properties. The last six mixtures were casted in order to test how the amount of fine particles (not exceeding 0.25 mm in diameter) influences the concrete mixture's technological properties.

Santrauka

Pagrindinis šio tyrimo tikslas – nustatyti, kaip mineralinių užpildų koncentracija veikia technologines betono mišinio savybes: slankumą, sklidumą, oro kiekį ir mišinio tankį. Iš viso buvo tirta 18 skirtingų betono mišinio sud≑čių. Pirmosios šešios sudėtys buvo analizuojamos siekiant nustatyti priklausomybę tarp smulkaus užpildo koncentracijos (smėlio frakcijos: 0/1 bei 0/4) ir technologinių betono mišinio savybių. Kitos šešios sudėtys buvo analizuojamos siekiant rasti priklausomybę tarp stambaus užpildo koncentracijos (žvirgždo frakcija 4/16) ir technologinių betono mišinio savybių. Paskutinės šešios betono mišinio sudėtys buvo analizuojamos siekiant nustatyti smulkiųjų dalelių, kurių skersmuo neviršija 0,25 mm, kiekio įtaką technologinėms betono mišinio savybėms.

Reikšminiai žodžiai: betono mišinio slankumas, betono mišinio tankis, sklidumo bandymas, oro kiekis

Keyword : concrete mixture slump, concrete mixture density, flow table test, air content